IC 401 12MM 33M IPT
Hersteller: IPT
Category: Insulating tapes
Description: Tape: electrical insulating; W: 12mm; L: 33m; Thk: 0.18mm; white
Thickness: 0.18mm
Dielectric strength: 3kV
Width: 12mm
Adhesion to steel: 7N/cm
Elongation at rupture: 5%
Length: 33m
Tensile strength: 160N/cm
Max ambient temperature: 200°C
Resistance to: tearing; temperature
Colour: white
Tape application: high temperature applications; winding insulation
Tape features: good adhesion to uneven surfaces; high mechanical strength; leaves no glue residue after remove
Kind of adhesive: silicone
Type of tape: electrical insulating
Tape material: glass cloth
Category: Insulating tapes
Description: Tape: electrical insulating; W: 12mm; L: 33m; Thk: 0.18mm; white
Thickness: 0.18mm
Dielectric strength: 3kV
Width: 12mm
Adhesion to steel: 7N/cm
Elongation at rupture: 5%
Length: 33m
Tensile strength: 160N/cm
Max ambient temperature: 200°C
Resistance to: tearing; temperature
Colour: white
Tape application: high temperature applications; winding insulation
Tape features: good adhesion to uneven surfaces; high mechanical strength; leaves no glue residue after remove
Kind of adhesive: silicone
Type of tape: electrical insulating
Tape material: glass cloth
auf Bestellung 8 Stücke:
Lieferzeit 14-21 Tag (e)
| Anzahl | Preis |
|---|---|
| 6+ | 12.14 EUR |
| 7+ | 11.23 EUR |
Produktrezensionen
Produktbewertung abgeben
Technische Details IC 401 12MM 33M IPT
Category: Insulating tapes, Description: Tape: electrical insulating; W: 12mm; L: 33m; Thk: 0.18mm; white, Thickness: 0.18mm, Dielectric strength: 3kV, Width: 12mm, Adhesion to steel: 7N/cm, Elongation at rupture: 5%, Length: 33m, Tensile strength: 160N/cm, Max ambient temperature: 200°C, Resistance to: tearing; temperature, Colour: white, Tape application: high temperature applications; winding insulation, Tape features: good adhesion to uneven surfaces; high mechanical strength; leaves no glue residue after remove, Kind of adhesive: silicone, Type of tape: electrical insulating, Tape material: glass cloth.