IC 401 25MM 33M IPT
Hersteller: IPT
Category: Insulating tapes
Description: Tape: electrical insulating; W: 25mm; L: 33m; Thk: 0.18mm; white
Colour: white
Width: 25mm
Length: 33m
Resistance to: tearing; temperature
Thickness: 0.18mm
Dielectric strength: 3kV
Type of tape: electrical insulating
Kind of adhesive: silicone
Adhesion to steel: 7N/cm
Tape features: good adhesion to uneven surfaces; high mechanical strength; leaves no glue residue after remove
Tape application: high temperature applications; winding insulation
Tensile strength: 160N/cm
Max ambient temperature: 200°C
Elongation at rupture: 5%
Tape material: glass cloth
Category: Insulating tapes
Description: Tape: electrical insulating; W: 25mm; L: 33m; Thk: 0.18mm; white
Colour: white
Width: 25mm
Length: 33m
Resistance to: tearing; temperature
Thickness: 0.18mm
Dielectric strength: 3kV
Type of tape: electrical insulating
Kind of adhesive: silicone
Adhesion to steel: 7N/cm
Tape features: good adhesion to uneven surfaces; high mechanical strength; leaves no glue residue after remove
Tape application: high temperature applications; winding insulation
Tensile strength: 160N/cm
Max ambient temperature: 200°C
Elongation at rupture: 5%
Tape material: glass cloth
auf Bestellung 26 Stücke:
Lieferzeit 14-21 Tag (e)
| Anzahl | Preis |
|---|---|
| 3+ | 24.1 EUR |
| 4+ | 22.78 EUR |
Produktrezensionen
Produktbewertung abgeben
Technische Details IC 401 25MM 33M IPT
Category: Insulating tapes, Description: Tape: electrical insulating; W: 25mm; L: 33m; Thk: 0.18mm; white, Colour: white, Width: 25mm, Length: 33m, Resistance to: tearing; temperature, Thickness: 0.18mm, Dielectric strength: 3kV, Type of tape: electrical insulating, Kind of adhesive: silicone, Adhesion to steel: 7N/cm, Tape features: good adhesion to uneven surfaces; high mechanical strength; leaves no glue residue after remove, Tape application: high temperature applications; winding insulation, Tensile strength: 160N/cm, Max ambient temperature: 200°C, Elongation at rupture: 5%, Tape material: glass cloth.