RM-NT0003 LulzBot
Hersteller: LulzBot
Description: POLYMAKER POLYWOOD FILAMENT (1.7
Packaging: Bulk
Color: Wood
Tensile Strength: 23.2Mpa
Weight: 1.323 lb (600.0 g)
Operating Temperature: 190°C ~ 210°C
Part Status: Active
Density: 0.8g/cm³
Filament Diameter: 0.070" (1.75mm)
Flex Strength: 52.9Mpa
Description: POLYMAKER POLYWOOD FILAMENT (1.7
Packaging: Bulk
Color: Wood
Tensile Strength: 23.2Mpa
Weight: 1.323 lb (600.0 g)
Operating Temperature: 190°C ~ 210°C
Part Status: Active
Density: 0.8g/cm³
Filament Diameter: 0.070" (1.75mm)
Flex Strength: 52.9Mpa
auf Bestellung 4 Stücke:
Lieferzeit 10-14 Tag (e)
Anzahl | Preis ohne MwSt |
---|---|
1+ | 52.78 EUR |
Produktrezensionen
Produktbewertung abgeben
Technische Details RM-NT0003 LulzBot
Description: POLYMAKER POLYWOOD FILAMENT (1.7, Packaging: Bulk, Color: Wood, Tensile Strength: 23.2Mpa, Weight: 1.323 lb (600.0 g), Operating Temperature: 190°C ~ 210°C, Part Status: Active, Density: 0.8g/cm³, Filament Diameter: 0.070" (1.75mm), Flex Strength: 52.9Mpa.