RT625 908-52155 WACKER

Category: Encapsulating materials
Description: Silicone encapsulating compound; translucent; 1.1g/cm3@20°C
Density: 1.1g/cm3 @ 20°C
Type of chemical agent: silicone encapsulating compound
Kind of package: can
Weight mixing ratio: 9:1
Dynamic viscosity: 12000mPas
Curing method: RTV
Application: sealing and tightening
Colour: translucent
Agent features: two-component; very low contraction while curing
Tensile strength: 6.5N/mm2
Bonding time: 60min
Shore hardness: 25
Elongation at rupture: 600%
Net weight: 1kg
Anzahl je Verpackung: 1 Stücke
Produkt ist nicht verfügbar
Produktrezensionen
Produktbewertung abgeben
Technische Details RT625 908-52155 WACKER
Category: Encapsulating materials, Description: Silicone encapsulating compound; translucent; 1.1g/cm3@20°C, Density: 1.1g/cm3 @ 20°C, Type of chemical agent: silicone encapsulating compound, Kind of package: can, Weight mixing ratio: 9:1, Dynamic viscosity: 12000mPas, Curing method: RTV, Application: sealing and tightening, Colour: translucent, Agent features: two-component; very low contraction while curing, Tensile strength: 6.5N/mm2, Bonding time: 60min, Shore hardness: 25, Elongation at rupture: 600%, Net weight: 1kg, Anzahl je Verpackung: 1 Stücke.
Weitere Produktangebote RT625 908-52155
Foto | Bezeichnung | Hersteller | Beschreibung |
Verfügbarkeit |
Preis |
---|---|---|---|---|---|
![]() |
RT625 908-52155 | Hersteller : WACKER |
![]() Description: Silicone encapsulating compound; translucent; 1.1g/cm3@20°C Density: 1.1g/cm3 @ 20°C Type of chemical agent: silicone encapsulating compound Kind of package: can Weight mixing ratio: 9:1 Dynamic viscosity: 12000mPas Curing method: RTV Application: sealing and tightening Colour: translucent Agent features: two-component; very low contraction while curing Tensile strength: 6.5N/mm2 Bonding time: 60min Shore hardness: 25 Elongation at rupture: 600% Net weight: 1kg |
Produkt ist nicht verfügbar |