F3211/8 BK103 Alpha Wire
Hersteller: Alpha Wire
Description: HEATSHRINK 1/8" X 4' BLACK
Features: Abrasion Resistant, Adhesive Lined, Chemical Resistant, Fluid Resistant, Heat Resistant, UV Resistant, Water Resistant
Packaging: Bulk
Color: Black
Material: Polyolefin (PO)
Length: 4.00' (1.22m)
Type: Tubing, Flexible
Operating Temperature: -55°C ~ 125°C
Shrinkage Ratio: 3 to 1
Inner Diameter - Supplied: 0.125" (3.18mm)
Inner Diameter - Recovered: 0.040" (1.02mm)
Recovered Wall Thickness: 0.037" (0.94mm)
Shrink Temperature: 110°C
Storage/Refrigeration Temperature: 65°F ~ 95°F (18°C ~ 35°C)
Shelf Life: 60 Months
Description: HEATSHRINK 1/8" X 4' BLACK
Features: Abrasion Resistant, Adhesive Lined, Chemical Resistant, Fluid Resistant, Heat Resistant, UV Resistant, Water Resistant
Packaging: Bulk
Color: Black
Material: Polyolefin (PO)
Length: 4.00' (1.22m)
Type: Tubing, Flexible
Operating Temperature: -55°C ~ 125°C
Shrinkage Ratio: 3 to 1
Inner Diameter - Supplied: 0.125" (3.18mm)
Inner Diameter - Recovered: 0.040" (1.02mm)
Recovered Wall Thickness: 0.037" (0.94mm)
Shrink Temperature: 110°C
Storage/Refrigeration Temperature: 65°F ~ 95°F (18°C ~ 35°C)
Shelf Life: 60 Months
auf Bestellung 158 Stücke:
Lieferzeit 21-28 Tag (e)
Anzahl | Preis ohne MwSt |
---|---|
1+ | 64.56 EUR |
5+ | 54.37 EUR |
10+ | 49.27 EUR |
25+ | 45.87 EUR |
50+ | 44.17 EUR |
100+ | 43.15 EUR |
Produktrezensionen
Produktbewertung abgeben
Technische Details F3211/8 BK103 Alpha Wire
Description: HEATSHRINK 1/8" X 4' BLACK, Features: Abrasion Resistant, Adhesive Lined, Chemical Resistant, Fluid Resistant, Heat Resistant, UV Resistant, Water Resistant, Packaging: Bulk, Color: Black, Material: Polyolefin (PO), Length: 4.00' (1.22m), Type: Tubing, Flexible, Operating Temperature: -55°C ~ 125°C, Shrinkage Ratio: 3 to 1, Inner Diameter - Supplied: 0.125" (3.18mm), Inner Diameter - Recovered: 0.040" (1.02mm), Recovered Wall Thickness: 0.037" (0.94mm), Shrink Temperature: 110°C, Storage/Refrigeration Temperature: 65°F ~ 95°F (18°C ~ 35°C), Shelf Life: 60 Months.