RT-3-NO.2-0-1IN TE Connectivity Raychem Cable Protection
Hersteller: TE Connectivity Raychem Cable Protection
Description: HEATSHRINK 0.319" X 0.083' BLACK
Packaging: Bulk
Features: Abrasion Resistant, Chemical Resistant, Flame Retardant, Solvent Resistant, Strain Resistant
Color: Black
Material: Polyolefin (PO), Irradiated
Length: 0.083' (25.40mm, 1.00")
Type: Tubing, Semi Rigid
Operating Temperature: -55°C ~ 135°C
Shrinkage Ratio: 2.5 to 1
Inner Diameter - Supplied: 0.319" (8.10mm)
Inner Diameter - Recovered: 0.125" (3.18mm)
Recovered Wall Thickness: 0.031" (0.79mm)
Shrink Temperature: 110°C
Part Status: Active
Storage/Refrigeration Temperature: 32°F ~ 95°F (0°C ~ 35°C)
Shelf Life: 144 Months
| Anzahl | Preis |
|---|---|
| 125+ | 0.14 EUR |
| 167+ | 0.11 EUR |
| 186+ | 0.095 EUR |
| 203+ | 0.087 EUR |
| 226+ | 0.078 EUR |
| 245+ | 0.072 EUR |
| 274+ | 0.064 EUR |
| 500+ | 0.059 EUR |
| 1000+ | 0.054 EUR |
Produktrezensionen
Produktbewertung abgeben
Technische Details RT-3-NO.2-0-1IN TE Connectivity Raychem Cable Protection
Description: HEATSHRINK 0.319" X 0.083' BLACK, Packaging: Bulk, Features: Abrasion Resistant, Chemical Resistant, Flame Retardant, Solvent Resistant, Strain Resistant, Color: Black, Material: Polyolefin (PO), Irradiated, Length: 0.083' (25.40mm, 1.00"), Type: Tubing, Semi Rigid, Operating Temperature: -55°C ~ 135°C, Shrinkage Ratio: 2.5 to 1, Inner Diameter - Supplied: 0.319" (8.10mm), Inner Diameter - Recovered: 0.125" (3.18mm), Recovered Wall Thickness: 0.031" (0.79mm), Shrink Temperature: 110°C, Part Status: Active, Storage/Refrigeration Temperature: 32°F ~ 95°F (0°C ~ 35°C), Shelf Life: 144 Months.
Weitere Produktangebote RT-3-NO.2-0-1IN nach Preis ab 0.049 EUR bis 0.15 EUR
| Foto | Bezeichnung | Hersteller | Beschreibung |
Verfügbarkeit |
Preis | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
RT-3-NO.2-0-1IN | Hersteller : TE Connectivity / Raychem |
Heat Shrink Tubing & Sleeves HS-TUBING .32" BK PRICE PER PC |
auf Bestellung 16436 Stücke: Lieferzeit 10-14 Tag (e) |
|